JIANGSU MOER INTELLIGENT EQUIPMENT CO.，LTD
Pleater Master, Worlder Leader
Add to Cart
|
Items |
Part A |
Part B |
|
|
Before curing |
Appearance |
white |
brown |
|
Viscosity(mPa.s) |
22000±5000 |
200±50 |
|
|
Density(g/cm3) |
1.70±0.05 |
1.22-1.25 |
|
|
Use ration by weight A:B |
6:1 |
||
|
|
Viscosity after mixing |
3500±500 adjustable |
|
|
Operation time(min,25℃) |
30 adjustable |
||
|
Turnover time(min,25℃) |
150 adjustable |
||
|
Curing time(h,25℃) |
24 |
||
|
After curing |
Light yellow |
||
|
Shear strength(N/mm) |
19.85 |
||
|
Max peel force(N) |
990.63 |
||
|
Max peel strength(N/mm) |
99.06 |
||
|
Average peel force(N) |
717.77 |
||
|
Average peel strength(N/mm) |
71.78 |
||
|
Min peel force(N) |
455.87 |
||
|
Min peel strength(N/mm) |
45.59 |
||
Features:
1.Two component filter cartridge adhesive is especially suitable for plastic or metal end cap sealing in hydraulic oil filter elements, dust filter elements, industrial filters, oil filters, fuel filters and other products.
2.Two Component Filter Cartridge Adhesive is suitable for air purification filters. It is non-toxic, odorless, has good fluidity, is easy to operate, and has a smooth surface after curing, good toughness, shock resistance, pressure resistance, and is not easy to break.
Project Indicators:
Hardness (Shore A) 50±5
Water absorption (%) ≤0.1
Tensile strength (Mpa) ≥0.6
Usage:
1. Weigh components A and B in a container according to the weight ratio A:B=2:1 and stir evenly.
2. Start injecting glue after stirring evenly.
Precautions:
1. Both components A and B must be sealed and stored to avoid long-term contact with air.
2. Mixing containers and stirring tools must be sealed and stored to avoid long-term contact with air.
3. When the ambient temperature is lower than 10℃, the viscosity of components A and B will increase significantly. When using, the stirring time should be appropriately increased to ensure uniform stirring.
FAQ
1.There are many types of polyurethane filter element glue, which can be roughly divided into two categories, namely two-component polyurethane adhesive and single-component polyurethane adhesive. The detailed introduction includes two-component foaming glue, two-component glue stock solution, two-component non-foaming glue, two-component PU glue and single-component foaming glue, thermosetting glue, etc. Although there are some differences in types and names, the functions used are similar.
2.The appearance of the filter element glue is off-white liquid and light brown solid. The two colloids can be blended in the ratio of 8:1, 6:1, 100:40, 100:35, 100:33, 100:25, and can be bonded to various materials such as iron covers, filter paper, filter cloth, plastic covers, etc. However, during the bonding process, attention should be paid to the cleanliness of the surface of the object, without stains and impurities, and it should be applied with a roller or brush. Another point to note is that you can blend as much colloid as you need, and use it up within 50 minutes. You must use resources reasonably. Just stick the objects together, then squeeze out the excess colloid, grasp the appropriate time, and gently bond the objects. This kind of colloid that has been blended in a certain ratio should not be stored for a long time, as too long a time will affect the best effect of the colloid.